Nacházíte se :: Hlavní stránka » Products » Epoxy adhesives » Epoxy adhesives

Epoxy adhesives

 

Epoxy adhesives LETOXIT® covers complete adhesive range suitable for bonding of all possible materials. Individual types are different in pot life, curing time, shear strengths or temperature resistance. Epoxy adhesives generally dominate  in excellent  mechanical characteristics, moisture resistance and low/high temperature resistance.

 


Epoxy adhesives LETOXIT®  covers whole product range for qluing of all possible materials such as wood, glassfiber, metals, glass or plastics (ABS, PE, PS)

 

Nowaday are our epoxy adhesives LETOXIT® mostly using for production of sport equipment (ski, icehockey sticks or snowboards). In case you are looking for high strength qluing (in aviation, automotive), we produce epoxy adhesives with extra high strength LETOXIT KFL and LETOXIT PL.

 

 Epoxy adhesives in cartridges

 

ADHESIVE CHARACTERISTICS USAGE

LH 214

NEW!

universal tough tixotropic adhesive with great adhesion and with high shear strength. Suitable for application, where uses Araldit 2014

  • mix ratio 2:1
  • thixotropic
  • pot life: 50 min.
  • Tg: 95 °C (postcured at 80°C)
  • curing at room temperature
  • shear strength: 20 MPa
  • final strength in 3 days
  • package cartridge 400 ml

metals

composites

wood

ceramics

 

all-round

LH 83

universal pastelike epoxy sealant for filling space up to 10 mm

  • mix ratio 1:1
  • thixotropic
  • pot life: 30 - 40 min.
  • Tg: 70 °C
  • shear strength: 14 MPa
  • manipulation strength in 4 hours.
  • final strength in 48 hours
  • package cartridge 200 ml

 

metals

composites

plastics

wood

 

all-round application

LH 205

 

fast curing fixing epoxy adhesive - 5 min.

  • mix ratio 1:1
  • transparent
  • solvent free
  • pot life: 5 min.
  • Tg: 50 °C
  • shear strength: 25 MPa
  • manipulation strength in 15 min.
  • final strength in 60 min.
  • package cartridge 50 ml

 

metals

composites

plastics

wood

 

all-round application

LH 186

 

 fast curing epoxy adhesive - 30 min.
  • mix ratio 1:1
  • transparent
  • solvent free
  • pot life: 30 min.
  • Tg: 50 °C
  • shear strength: 14 MPa
  • manipulation strength in 60 min.
  • final strength in 3 hours
  • package cartridge 200 ml

metals

composites

plastics

wood

 

all-round application

 

LH 21

high quality epoxy adhesive for all-round application, GOOD PRICE!

  • mix ratio 2:1
  • thixotropic
  • extra high shear strength
  • pot life: 60 min.
  • Tg: 50 °C
  • shear strength: 25 MPa
  • manipulation strength in 24 hours
  • final strength in 48 hours
  • package cartridge 400 ml

metals

composites

plastics

wood

 

all-round application

PL 50

epoxy adhesives for EXTRA high strength joints.

  • mix ratio 2:1
  • excellent mechanicaů properties of final joint
  • pot life: 60 - 90 min.
  • Tg: 50 °C
  • shear strength: 36 MPa
  • manipulation strength in 24 hours
  • final strength in 4 - 5 days
  • package cartridge 50 ml

metals

composites

plastics

wood

 

all-round application

 Leaflet for 2-component epoxy adhesives (507 kB)

 

 

 

Epoxy adhesives

ADHESIVE CHARACTERISTICS USAGE

LH 21

basic type

  • curing for 48 h at room temperature
  • mix ratio 2:1
  • tixotropic (doesnt  flow off)
  • pot life: 60 min.
  • Tg (max): 50 °C (70°C)
  • shear strength: 20-25 MPa
  • handling after 24 h
  • final strenght in 3 days

wood

hard foams

composites

 

 

allround application

LH 22

 

lower viscosity (better for rough sufraces)

  • curing for 48 h at room temperature
  • mix ratio 2:1
  • pot life: 60 min.
  • Tg (max): 50 °C (70°C)
  • shear strength: 20-25 MPa
  • handling after 24 h
  • final strenght in 3 days

wood

hard foams

composites

 

 

allround application

 

LH 161

one component extra light adhesive/sealant, FAR 25

  • curing 60 min at 120 -125 °C
  • tixotropic (doesnt flow off)
  • density: 0,695 g/m3
  • pot life: 168 hours
  • Tg: 120 °C
  • tensile strength: 54 MPa
  • fulfills FAR 25
  

metals

 

 

aviation

(sealing of sandwich panel edges)

 

Epoxy laminating adhesives

Product range of epoxy laminating adhesives covers many special types, which are used mainly for production of sport equipment (ski, snowboard, ice sticks). The combination of gluing and lamination (impregnation of materials) in one step brings great advantage for production due to faster and easier manufacturing process.

   

 

ADHESIVE CHARACTERISTICS USAGE

LHX 038

black colour

  • curing 48 h at room temperature
  • mix ratio 100:33
  • tixotropic (doesnt flow off)
  • pot life: 60 min.
  • Tg (max): 50 °C (70°C)
  • shear strength: 20 MPa
  • handling in 24 hours
  • final strength in 3 days

metals

wood

foams

composites

PS, ABS, PE

 

snowboards

LHX 043

white colour

  • curing 10-20 min at 80 °C
  • mix ratio 100:34
  • tixotropic (doesnt flow off)
  • pot life: 60 min.
  • Tg (max): 60 °C (70°C)
  • shear strength: 20 MPa
  • handling in 24 hours
  • final strength in 3 days

metals

wood

foams

composites

PS, ABS, PE

 

cross-country ski

 LHX 091

fast curing

  • curing 6 - 8 min at 80 °C
  • mix ratio 4:1
  • tixotropic (doesnt flow off)
  • pot life: 15 min.
  • Tg (max): 60 °C (85°C)
  • shear strength: 20 MPa
  

metals

wood

foams

composites

PS, ABS, PE

 

ski

LHX 092

 for titanal gluing

  • curing 13 - 18 min at 80 °C
  • mix ratio 5:2
  • tixotropic (doesnt flow off)
  • pot life: 60 - 70 min.
  • Tg (max): 60 °C (70°C)
  • shear strength: 20 MPa
  

metals

wood

foams

composites

PS, ABS, PE


LHX 103

 transparent colour

  • curing 10 - 15 min at 80 °C
  • mix ratio 100:46
  • tixotropic (doesnt flow off)
  • pot life: 60 - 70 min.
  • Tg (max): 60 °C (78°C)
  • shear strength: 20 - 25 MPa

metals

wood

foams

composites

PS, ABS, PE

LHX 105

 extra high shear strength

  • curing 13 - 16 min. at 80°C
  • mix ratio 100:40
  • tixotropic (doesnt flow off)
  • pot life: 45 - 55 min.
  • Tg (max): 60 °C (70°C)
  • shear strength: 25 MPa

metals

wood

foams

composites

PS, ABS, PE

LHX 143

 titanal gluing, low viscosity

  • curing 13 - 18 min. at 80 °C
  • possible curing at room temperature
  • mix ratio 100:40
  • nontixotropic (flow off)
  • pot life: 60 - 70 min.
  • Tg (max): 60 °C (70°C)
  • shear strength: 20 - 25 MPa

metals

wood

foams

composites

PS, ABS, PE

LHX 173

titanal gluing, high impregnation ability

  • curing 13 - 18 min. at 80 °C
  • mix ratio 100:40
  • nontixotropic (flow off)
  • pot life: 60 - 70 min.
  • Tg (max): 60 °C (70°C)
  • shear strength: 20 - 25 MPa

metals

wood

foams

composites

PS, ABS, PE

 

 

Download

 Table - Technical datas LETOXIT® (35 kB)

 

 

 